Effects of Co ratio on fatigue life of WC-Co die inserts used in cold forming operations
27th International ESAFORM Conference on Material Forming, ESAFORM 2024, Toulouse, Fransa, 24 - 26 Nisan 2024, cilt.41, ss.881-890, (Tam Metin Bildiri)
- Yayın Türü: Bildiri / Tam Metin Bildiri
- Cilt numarası: 41
- Doi Numarası: 10.21741/9781644903131-96
- Basıldığı Şehir: Toulouse
- Basıldığı Ülke: Fransa
- Sayfa Sayıları: ss.881-890
- Anahtar Kelimeler: WC-Co, Co Ratio, Fatigue Life, Cold Forming
- Dokuz Eylül Üniversitesi Adresli: Evet
Özet
Production of fasteners via cold forming requires high forming forces, which induce significant stresses in dies. Therefore, die performance becomes a critical parameter of the fastener production process. Estimation of die life with high accuracy allows to enhance production efficiency and reduce die-related expenditures. Generally, WC-Co hardmetals consisting of 4-30% Co content as a binder are highly preferred in cold forming operations. WC-Co metal-ceramic composite materials offer high wear resistance against frictional forces, high compressive strength, and lower elastic deformation to resist excessive contact pressures, which are primary requirements for cold-forming dies. In this study, experimental investigations were conducted for the determination and comparison of fatigue performance at three different stress amplitudes, utilizing three-point bending fatigue testing with two different grades of WC-Co hardmetals. After the experiments, Goodman-Haigh diagrams were obtained from the experimental results to be utilized in predictive die-life calculations.