Effect of Aggregate Type on Mechanical Properties of Reactive Powder Concrete

Aydın S., Yazıcı H., Yardimci M. Y., Yiğiter H.

ACI MATERIALS JOURNAL, cilt.107, sa.5, ss.441-449, 2010 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 107 Sayı: 5
  • Basım Tarihi: 2010
  • Dergi Adı: ACI MATERIALS JOURNAL
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.441-449
  • Anahtar Kelimeler: aggregate, autoclave, fracture energy, reactive powder concrete, scanning electron microscopy, steam curing, HIGH-PERFORMANCE CONCRETE, HIGH-STRENGTH CONCRETE, COARSE-AGGREGATE, CURING CONDITIONS, BEHAVIOR, MODULUS, SURFACE
  • Dokuz Eylül Üniversitesi Adresli: Evet

Özet

This paper focuses on the experimental study of the mechanical properties of reactive powder concrete (RPC) produced with different aggregates, such as korund, basalt, limestone, quartz, sintered bauxite, and granite. The effects of aggregate type on mechanical properties were investigated under standard, atmospheric, and high-pressure steam curing. The test results indicate that very high compressive strength can be achieved even with low-strength or smooth-surface aggregates; however superior flexural performance requires high-strength aggregate with rough surface characteristics. A compressive strength of approximately 200 MPa (29 ksi) can be obtained when strong and rough-surface textured aggregate were used under standard curing conditions. Atmospheric and high-pressure steam curing improved the compressive strength significantly. These curing regimes, however did not considerably improve the flexural performance. Pressure application in fresh state resulted in a great improvement of the compressive strength of RPC, particularly in the case of high-strength and rough-surface textured aggregates. In this way, a compressive strength over 400 MPa (58 ksi) was obtained with bauxite aggregate after pressure application and autoclaving.