The effect of anodization parameters on the formation of nanoporous TiO2 layers and their photocatalytic activities

EROL M., DİKİCİ T., Toparli M., Celik E.

JOURNAL OF ALLOYS AND COMPOUNDS, cilt.604, ss.66-72, 2014 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 604
  • Basım Tarihi: 2014
  • Doi Numarası: 10.1016/j.jallcom.2014.03.105
  • Dergi Adı: JOURNAL OF ALLOYS AND COMPOUNDS
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.66-72
  • Anahtar Kelimeler: Nanoporous TiO2, Anodization parameters, Photocatalytic activity, Surface morphology, TITANIA NANOTUBES, PHASE, WATER, TEMPERATURE, DEGRADATION, MORPHOLOGY
  • Dokuz Eylül Üniversitesi Adresli: Evet

Özet

In this work, nanoporous titanium dioxide (TiO2) layers were successfully formed by electrochemical anodization method on titanium (Ti) surface in fluorine containing electrolytes with different processing parameters. The effects of anodization voltages, electrolyte temperature and anodization time on the microstructure and photocatalytic performance of nanoporous TiO2 layers were investigated and compared in details. Nanoporous structures were annealed at 480 degrees C for 2 h in air in order to obtain anatase transformation and increase crystallinity. The phase structure and surface morphology of the samples characterized by means of X-ray diffraction (XRD) and scanning electron microscope (SEM) respectively. The photocatalytic activity tests of the samples were evaluated by the degradation of aqueous methylene blue (MB) solutions under UV light illumination for different periods of time. The results showed that the processing parameters on production of nanoporous TiO2 layers played important roles in the degradation of aqueous MB solutions. To sum up, the highest photocatalytical activity was obtained at the sample anodized under 30 V for 30 min at 20 degrees C among the samples. (C) 2014 Elsevier B.V. All rights reserved.