JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, cilt.22, sa.10, ss.3024-3033, 2013 (SCI-Expanded)
Twin roll cast EN AW Al-Mn1Cu plates were butt welded with the friction stir welding process which employed a non-consumable tool, tilted by 1.5A degrees and 3A degrees with respect to the plate normal, rotated in a clockwise direction at 400 and 800 rpm, while traversing at a fixed rate of 80 mm/min along the weld line. Microstructural observations and microhardness tests were performed on sections perpendicular to the tool traverse direction. Tensile tests were carried out at room temperature on samples cut perpendicular to the weld line. The ultimate tensile strength of the welded EN AW Al-Mn1Cu plates improved with increasing tool rotation speed and decreasing tool tilt angle. This marked improvement in ultimate tensile strength is attributed to the increase in the heat input owing to an increased frictional heat generation. There appears to be a perfect correlation between the ultimate tensile strength and the size of the weld zone. The fracture surfaces of the base plate and the welded plates are distinctly different. The former is dominated by dimples typical of ductile fractures. A vast majority of the intermetallic particles inside the weld zones are too small to generate dimples during a tensile test. The fracture surface of the welded plates is thus characterized by occasional dimples that are elongated in the same direction suggesting a tensile tearing mechanism.