A mathematical approach for borax mineral in thermal process

Creative Commons License

Özel M.

6. Endüstriyel Hammaddeler Sempozyumu, İzmir, Türkiye, 1 - 03 Şubat 2007, ss.334-340

  • Yayın Türü: Bildiri / Tam Metin Bildiri
  • Basıldığı Şehir: İzmir
  • Basıldığı Ülke: Türkiye
  • Sayfa Sayıları: ss.334-340
  • Dokuz Eylül Üniversitesi Adresli: Evet

Özet

ABSTRACT: In this study a mathematical model is developed to determine the required temperature and

duration period prior to heat treatment. In the experimental studies, a series of systematic thermal

experiments have been carried out in a muffle furnace. The growth behavior of borax was investigated at

different temperatures with changing heating times and particle size. Borax samples have been examined,

weighted and measured next to the heating process. The mathematical test results obviously revealed that

statistically there was a direct correlation between the optimum expansion of borax with heating time and

temperature.

ÖZET: Bu çalışmada kalsinasyon işlemi öncesi gerekli sıcaklık ve süreyi belirlemek üzere matematiksel bir

model geliştirilmiştir. Deneysel çalışmalarda sabit muffle fırında bir dizi sistematik sıcaklık denemeleri

gerçekleştirilmiştir. Boraksın, değişen sıcaklık, zaman ve tane boyutlarındaki genleşme eğilimi

incelenmiştir. Boraks örnekleri, ısıtma işlemleri sonrasında incelenmiş, tartılmış ve ölçülmüştür.

Matematiksel test sonuçları, optimal genleşmenin ısıtma süresi ve sıcaklıkla doğrudan ilişkili olduğunu

istatiksel olarak açıkça göstermiştir.